A 100% solids, solvent-free, two component polyurethane adhesive system with a viscosity of 2,500-3,500 cPs.
Mor-Free™ L 75-164 is a two-component polyurethane adhesive system that is solvent-free and 100% solids, that can be applied at room temperature. As the reactivity of Mor-Free L 75-164 is high, the laminates can generally be further processed in as little as six hours. The chemical curing is generally completed within 3 days using C-411 co-reactant or 5 days using C-132-2 at room temperature (72 °F).
Application Method : Smooth roll transfer
Coreactant : C132-2, C-411
Coating Weight : 0.8-1.3 lbs/ream
Chemistry : Polyurethane
Color: Clear Yellow Liquid
Density: 9.5 lbs/gallon
Mix Ratio: 100:63 with C-132-2, 100:40 with C-411
Shelf Life: 360 days
Applied Solids: 100 %
Supplied Solids: 100 %
Cure Time: 5 days at 77 °F
Mixed Viscosity: 1,300 cPs @ 110 °F
Nip Temperature: 120-140 °F
Nominal Application Temperature: 122-140 °F
Post Process Time: 4-8 hrs time to slit
Pot Life : 45 minutes at 110 °F
Viscosity: 2,500-3,500 cPs
Primary Chemistry: Polyurethane
Rapid bond development to decrease time needed for processing
Adhesion to high slip films
High heat resistance
Low nip temperature
Adhesion to foil and metallized films
High chemical resistance
Fast slitting time
Used for a wide range of applications including hot fill and boil-in-bag. Polyolefin films, including LDPE to LDPE, OPP to OPP, and OPP to LDPE, as well as Nylon, Polyester, and other packaging substrates. The films may be unprinted, or reverse printed with the appropriate laminating grade inks.
Dow Laminating Adhesives is a wide-reaching portfolio of adhesives and coatings for the flexible packaging and industrial lamination markets. They include the latest innovations in bio-friendly water-based, solventless and specialty adhesives for nearly every packaging application - from general purpose through high performance, including new cold seal, heat-seal and clear retort adhesives.