Specifications

Density: 1.26 g/cm³
Density, specific gravity: 1.26 g/cm³
Change in volume (in reference fuel B, 27°C, 168 hrs): 32%
Change in volume (in ASTM #1 oil, 100°C, 168 hrs): −9.0%
Change in volume (in IRM 903 oil, 100°C, 168 hrs): 30%
Change in volume (in water, 100°C, 168 hrs): 14%
Melt viscosity (190°C, 300 sec−1): 580 Pa·s
Tensile stress at 100% (1.90 mm): 4.10 MPa
Tensile stress at 100% (125°C, 1.90 mm): 4.50 MPa
Tensile stress at yield (1.90 mm): 8.90 MPa
Tensile stress at yield (125°C, 1.90 mm): 8.90 MPa
Tensile strength at yield (1.90 mm): 8.90 MPa
Tensile strength at yield (125°C, 1.90 mm): 8.90 MPa
Tensile strain at break (1.90 mm): 400%
Tensile strain at break (125°C, 1.90 mm): 370%
Torsion modulus (24°C, 1.9 mm): 2.1 MPa
Torsion modulus (−20°C, 1.9 mm): 45.5 MPa
Tensile set: 9%
Clash-Berg modulus (−23°C): 68.9 MPa
Tensile elongation at break (125°C, 1.90 mm): 370%
Tensile elongation at break (1.90 mm): 400%
Tear strength (Die C, 1.90 mm): 35.9 kN/m
Ductile/Brittle transition temperature: −45°C
Change in Shore hardness in air (Shore A, 125°C, 168 hrs): −2.0
Shore Hardness (Shore A, 1.90 mm, compression molded): 67
Change in durometer hardness in air (Shore A, 125°C, 168 hrs): −2.0
Durometer hardness (Shore A, 1.90 mm, compression molded): 67
Taber abrasion resistance (CS-17 Wheel, 1,000 g, 1,000 cycles): <1.00 mg
Processing (melt) temp: 177°C
Primary Chemistry: Melt-processable rubber resin