Form: Solid granules
Color: NAT – natural Color
Density 1.26 g/cm³ ISO 2781
Density - Specific Gravity 1.26 g/cm³ ASTM D471
Change in Volume
(in Reference Fuel B, 27 °C, 168 hr) 32 % ISO 1817
(in Reference Fuel B, 27 °C, 168 hr) 32 % ASTM D471
(in ASTM #1 Oil, 100 °C, 168 hr) -9.0 % ASTM D471
(in ASTM #1 Oil, 100 °C, 168 hr) -9.0 % ISO 1817
(in IRM 903 Oil, 100 °C, 168 hr) 30 % ISO 1817
(in IRM 903 Oil, 100 °C, 168 hr) 30 % ASTM D471
(in Water, 100 °C, 168 hr) 14 % ISO 1817
(in Water, 100 °C, 168 hr) 14 % ASTM D471
Melt Viscosity, (190 °C, 300 sec^-1) 580 Pa·s ASTM D3835
Tensile Stress at 100%
(1.90 mm) 4.10 MPa ISO 37
(1.90 mm) 4.10 MPa ASTM D412
(125 °C, 1.90 mm) 4.50 MPa ASTM D573
(125 °C, 1.90 mm) 4.50 MPa ISO 188
Tensile Stress at Yield
(1.90 mm) 8.90 MPa ISO 37
(125 °C, 1.90 mm) 8.90 MPa ISO 188
Tensile Strength at Yield
(1.90 mm) 8.90 MPa ASTM D412
(125 °C, 1.90 mm) 8.90 MPa ASTM D573
Tensile Strain at Break
(1.90 mm) 400 % ISO 37
(125 °C, 1.90 mm) 370 % ISO 188
Torsion Modulus
(24 °C, 1.9 mm) 2.1 MPa ASTM D1043
Compression Molded
(-20 °C, 1.9 mm) 45.5 MPa ASTM D1043
Compression Molded
Tensile Set 9 % ASTM D412
Clash-Berg Modulus, (-23 °C) 68.9 MPa ASTM D1043
Tensile Elongation at Break
(125 °C, 1.90 mm) 370 % ASTM D573
(1.90 mm) 400 % ASTM D412
Tear Strength, (Die C, 1.90 mm) 35.9 kN/m ASTM D624
Ductile/Brittle Transition Temperature -45 °C ASTM D746
Change in Shore Hardness in Air, (Shore A, 125 °C, 168 hr) -2.0 ISO 188
Shore Hardness, (Shore A, 1.90 mm, Compression Molded) 67 ISO 868
Change in Durometer Hardness in Air, (Shore A, 125 °C, 168
hr) -2.0 ASTM D573
Durometer Hardness, (Shore A, 1.90 mm, Compression
Molded) 67 ASTM D2240
Additional Information
Compression Set
(24 °C, 22 hr, Method B) 17 % ASTM D395
(100 °C, 22 hr, Method B) 69 % ASTM D395
(24 °C, 22 hr) 17 % ISO 815
(100 °C, 22 hr) 69 % ISO 815
Taber Abrasion Resistance, (CS-17 Wheel, 1000 g, 1000
Cycles) <1.00 mg ASTM D104
Primary Chemistry: Melt Processable Rubber