UCON™ Trident AW 68

Specifications

FZG visual gear test, stages passed (ASTM D5182 test method): 12
Four-ball EP test (ASTM D2783 test method)
Load wear index: 33.26
Last nonseizure, 80 kg (mm scar): 0.39
Last seizure, 126 kg (mm scar): 2.53
Weld load, kg: 160
V104 vane pump test, total mg wear (ASTM D7043 test method): <10
Viscosity @ 40°C, cSt (ASTM D445 test method): 68.0
Viscosity @ 100°C, cSt (ASTM D445 test method): 13.7
Viscosity @ 0°C, cSt (ASTM D445 test method): 614
Viscosity index (ASTM D2270 test method): 209
Flash point, Cleveland Open Cup, °C (ASTM D92 test method): 288
Flash point, Pensky Martens Closed Cup, °C (ASTM D93 test method): None
Fire point, °C (ASTM D92 test method): 322
FM approvals (test standard 6930): Approved
Specific gravity @ 20°C (ASTM D1298 test method): 1.041
Vapor pressure (mm Hg) (ASTM E1719 test method): <0.01
Specific heat (cal/g/°C) (ASTM E1269 test method): 0.478
Pour point, °C (ASTM D97 test method): −51
Ash content, % (ASTM D482 test method): 0.008
Corrosion protection, TORT (ASTM D665A test method): Pass
Copper strip corrosion (ISO 2160 test method): 1a, shiny
Aging behavior, hrs (DIN 51587 test method)
mg KOH/g: 0.31
Hours: 1,008
Coefficient of expansion (ASTM D1903 test method)
@ 20°C: 0.00079
@ 55°C: 0.00078
Weight, lbs/gal (20°C): 8.58;
Primary Chemistry: Polyalkylene glycol