Specifications

Density: 1.19 g/cm³
Density, specific gravity: 1.19 g/cm³
Change in volume (in reference fuel B, 27°C, 168 hrs): 30%
Change in volume (in ASTM #1 oil, 100°C, 168 hrs): −10%
Change in volume (in IRM 903 oil, 100°C, 168 hrs): 27%
Change in volume (in water, 100°C, 168 hrs): 12%
Melt viscosity (190°C, 300 sec−1): 545 Pa·s
Tensile stress at 100% (1.90 mm): 3.90 MPa
Tensile stress at 100% (125°C, 1.90 mm): 3.90 MPa
Tensile stress at yield (1.90 mm): 9.60 MPa
Tensile stress at yield (125°C, 1.90 mm): 10.6 MPa
Tensile strength at yield (1.90 mm): 9.60 MPa
Tensile strength at yield (125°C, 1.90 mm): 10.6 MPa
Tensile strain at break (1.90 mm): 300%
Tensile strain at break (125°C, 1.90 mm): 330%
Torsion modulus (24°C, 1.9 mm): 1.9 MPa
Torsion modulus (−20°C, 1.9 mm): 7.5 MPa
Tensile set: 8%
Clash-Berg modulus (−38°C): 68.9 MPa
Tensile elongation at break (125°C, 1.90 mm): 330%
Tensile elongation at break (1.90 mm): 300%
Tear strength (Die C, 1.90 mm): 26.3 kN/m
Ductile/Brittle transition temperature: −51°C
Change in Shore hardness in air (Shore A, 125°C, 168 hrs): 5.0
Shore hardness (Shore A, 1.90 mm, compression molded): 62
Change in durometer hardness in air (Shore A, 125°C, 168 hrs: 5.0
Durometer hardness (Shore A, 1.90 mm, compression molded): 62
Compression set (24°C, 22 hrs, Method B): 15%
Compression set (100°C, 22 hrs, Method B): 55%
Compression set (24°C, 22 hrs): 15%
Compression set (100°C, 22 hrs): 55%
Taber abrasion resistance (CS-17 Wheel, 1,000 g, 1,000 cycles): 7.00 mg
Melt temperature: 177°C
Primary Chemistry: Melt-processable rubber resin