Density: 1.10 g/cm³
Density, specific gravity: 1.10 g/cm³
Change in volume (in reference fuel B, 27°C, 168 hrs): 25%
Change in volume (in ASTM #1 oil, 100°C, 168 hrs): −19%
Change in volume (in IRM 903 oil, 100°C, 168 hrs): 16%
Change in volume (in water, 100°C, 168 hrs): 8.0%
Melt viscosity (190°C, 300 sec−1): 365 Pa·s
Tensile stress at 100% (1.90 mm): 2.90 MPa
Tensile stress at 100% (125°C, 1.90 mm): 2.70 MPa
Tensile stress at yield (1.90 mm): 8.00 MPa
Tensile stress at yield (125°C, 1.90 mm): 7.60 MPa
Tensile strength at yield (1.90 mm): 8.00 MPa
Tensile strength at yield (125°C, 1.90 mm): 7.60 MPa
Tensile strain at break (1.90 mm): 410%
Tensile strain at break (125°C, 1.90 mm): 390%
Torsion modulus (24°C, 1.9 mm): 2.2 MPa
Torsion modulus (−20°C, 1.9 mm): 5.9 MPa
Tensile set: 9%
Clash-Berg modulus (−40°C): 68.9 MPa
Tensile elongation at break (125°C, 1.90 mm): 390%
Tensile elongation at break (1.90 mm): 410%
Tear strength (Die C, 1.90 mm): 27.1 kN/m
Ductile/Brittle transition temperature: −87°C
Change in Shore hardness in air (Shore A, 125°C, 168 hrs): 4.0
Shore hardness (Shore A, 1.90 mm, compression molded): 59
Change in durometer Hardness in Air (Shore A, 125°C, 168 hrs): 4.0
Durometer hardness (Shore A, 1.90 mm, compression molded): 59
Compression set (24°C, 22 hrs, Method B): 13%
Compression set (100°C, 22 hrs, Method B): 62%
Compression set (24°C, 22 hrs): 13%
Compression set (100°C, 22 hrs): 62%
Taber abrasion resistance (CS-17 Wheel, 1,000 g, 1,000 cycles): 5.00 mg
Processing (melt) temp: 177°C
Primary Chemistry: Melt-processable rubber resin