Density: 1.12 g/cm³
Density, specific gravity: 1.12 g/cm³
Change in volume (in reference fuel B, 27°C, 168 hrs): 8%
Change in volume (in ASTM #1 oil, 100°C, 168 hrs): −30%
Change in volume (in IRM 903 oil, 100°C, 168 hrs): −6%
Change in volume (in water, 100°C, 168 hrs): 9.0%
Melt viscosity (190°C, 300 sec−1): 247 Pa·s
Tensile modulus (1.91 mm, compression molded): 3.0 MPa
Tensile strength at yield (1.91 mm, compression molded): 7.24 MPa
Tensile set: 12%
Tensile elongation at break (125°C, 1.90 mm): 340%
Tensile elongation at break (1.91 mm, compression molded): 380%
Tear strength (Die C, 1.90 mm): 26.3 kN/m
Ductile/Brittle transition temperature: −85°C
Change in Shore hardness in air (Shore A, 125°C, 168 hrs): 61
Durometer hardness (Shore A, 1.90 mm, compression molded): 60
Compression set (24°C, 22 hrs, Method B): 27%
Compression set (100°C, 22 hrs, Method B): 69%
Compression set (24°C, 22 hrs): 27%
Compression set (100°C, 22 hrs): 69%
Processing (melt) temp: 177°C
Primary Chemistry: Melt-processable rubber resin