Specifications

Density: 1.17 g/cm³
Specific gravity: 1.17 g/cm³
Change in volume (in reference fuel B, 27°C, 168 hrs): 32%
Change in volume (in ASTM #1 oil, 100°C, 168 hrs): −8.0%
Change in volume (in IRM 903 oil, 100°C, 168 hrs): 31%
Change in volume (in water, 100°C, 168 hrs): 5.0%
Melt viscosity (190°C, 300 sec−1): 700 Pa·s
Tensile stress at 100% (1.90 mm): 6.20 MPa
Tensile stress at 100% (125°C, 1.90 mm): 5.20 MPa
Tensile stress at yield (1.90 mm): 12.1 MPa
Tensile stress at yield (125°C, 1.90 mm): 11.0 MPa
Tensile strength at yield (1.90 mm): 12.1 MPa
Tensile strength at yield (125°C, 1.90 mm): 11.0 MPa
Tensile strain at break (1.90 mm): 320%
Tensile strain at break (125°C, 1.90 mm): 240%
Torsion modulus (24°C, 1.9 mm): 3.2 MPa
Torsion modulus (−20°C, 1.9 mm): 27.5 MPa
Tensile set: 10%
Clash-Berg modulus (−17°C): 68.9 MPa
Tensile elongation at break (125°C, 1.90 mm): 240%
Tensile elongation at break (1.90 mm): 320%
Tear strength (Die C, 1.90 mm): 35.0 kN/m
Ductile/Brittle transition temperature: −86°C
Change in Shore hardness in air (Shore A, 125°C, 168 hrs): −2.0
Shore hardness (Shore A, 1.90 mm, compression molded): 78
Change in durometer hardness in air (Shore A, 125°C, 168 hrs): −2.0
Durometer hardness (Shore A, 1.90 mm, compression molded): 78
Compression set (24°C, 22 hrs, Method B): 14%
Compression set (100°C, 22 hrs, Method B): 62%
Compression set (24°C, 22 hrs): 14%
Compression set (100°C, 22 hrs): 62%
Taber abrasion resistance (CS-17 Wheel, 1,000 g, 1,000 cycles): 3.00 mg
Processing (melt) temp: 177°C
Primary Chemistry: Melt-processable rubber