Density: 1.17 g/cm³
Density, specific gravity: 1.17 g/cm³
Change in volume (in ASTM #1 oil, 100°C, 168 hrs): −10%
Change in volume (in reference fuel B, 24°C, 168 hrs): 36%
Change in volume (in ASTM #3 oil, 100°C, 168 hrs): −23%
Tensile modulus (1.91 mm, compression molded): 6.41 MPa
Tensile stress at yield (1.91 mm, compression molded): 10.8 MPa
Tensile strength at yield (1.91 mm, compression molded): 10.8 MPa
Tensile strain at break (1.91 mm, compression molded): 320%
Tensile set: 13%
Clash-Berg modulus (−21°C): 68.9 MPa
Tensile elongation at break (1.91 mm, compression molded): 320%
Tear strength (24°C, Die C): 44.7 kN/m
Durometer hardness (Shore D, 1.91 mm, compression molded): 40
Compression set (24°C, 22 hrs, Method B): 27%
Compression set (100°C, 22 hrs, Method B): 74%
Compression set (24°C, 22 hrs): 27%
Compression set (100°C, 22 hrs): 74%
Taber abrasion resistance (CS-17 Wheel, 1,000 g, 1,000 cycles): 3.00 mg
Processing (melt) temp: 177°C
Primary Chemistry: Melt-processable rubber