LOCTITE® EA 9461 is an easily dispensable structural adhesive specially recommended for providing a tough, durable bond at room temperature between dissimilar materials. With a 1:1 mix ratio and a 40 minute pot life, it is ideal for a range of bonding applications, providing advanced performance and strength.
Resin properties:
Chemical type: epoxy
Appearance: white opaque paste
Specific gravity @ 25°C: 1.35
Viscosity, DIN 54453, mPa·s (cP), shear rate 10s¯¹: 85,980
Viscosity, DIN 54453, mPa·s (cP), shear rate 50s¯¹: 38,570
Thixotropic index: 2.8
Hardener properties:
Chemical type: Amine
Appearance: Black opaque paste
Specific gravity @ 25°C: 1.31
Viscosity, DIN 54453, mPa·s (cP), shear rate 10s¯¹: 59,530
Viscosity, DIN 54453, mPa·s (cP), shear rate 50s¯¹: 42,860
Thixotropic index: 2
Mixed properties:
Appearance: Gray paste
Pot life @ 22°C, minutes: 40
Fixture time, mixed, @ 22°C, minutes: 240
Shore hardness, ISO 868: 80
Elongation , ISO 527-2,%: 3.5
Tensile strength, ISO 527-2 N/mm² (psi): 30 (4,400)
Tensile modulus, ISO 527-2 N/mm² (psi): 2,757 (400,000)
Primary Chemistry:
Epoxy
LOCTITE® EA 9461 is a high-performance industrial adhesive that provides excellent bonding of dissimilar substrates, including metals and thermoset laminates. As a thixotropic epoxy, it exhibits excellent non-sag and fatigue resistance, effectively bonding surfaces with ease and curing quickly at room temperature to form a tough, durable bond. LOCTITE® EA 9461 fills gaps up to 3.0 mm and provides a tensile strength of 30 N/mm².
Resin properties:
Chemical type: epoxy
Appearance: white opaque paste
Specific gravity @ 25°C: 1.35
Viscosity, DIN 54453, mPa·s (cP), shear rate 10s¯¹: 85,980
Viscosity, DIN 54453, mPa·s (cP), shear rate 50s¯¹: 38,570
Thixotropic index: 2.8
Hardener properties:
Chemical type: Amine
Appearance: Black opaque paste
Specific gravity @ 25°C: 1.31
Viscosity, DIN 54453, mPa·s (cP), shear rate 10s¯¹: 59,530
Viscosity, DIN 54453, mPa·s (cP), shear rate 50s¯¹: 42,860
Thixotropic index: 2
Mixed properties:
Appearance: Gray paste
Pot life @ 22°C, minutes: 40
Fixture time, mixed, @ 22°C, minutes: 240
Shore hardness, ISO 868: 80
Elongation , ISO 527-2,%: 3.5
Tensile strength, ISO 527-2 N/mm² (psi): 30 (4,400)
Tensile modulus, ISO 527-2 N/mm² (psi): 2,757 (400,000)
Primary Chemistry:
Epoxy
Poor adherence of adhesive to dissimilar surfaces
Drip or sag of adhesive prior to cure
Bonding dissimilar substrates, including metal, motoring thermoplastics, and thermoset laminates
Gap filling