LOCTITE® EA 9514 is a single-component adhesive from Henkel that creates a tough bond line between filter and magnet applications, filling gaps up to 3.0mm. LOCTITE® EA 9514 can be cured using induction heating or conventional heat.
Appearance: Grey, opaque paste
Specific Gravity @ 25°C: 1.42 to 1.48
Yield Point @ 25°C, Pa•s: Haake PK 100, M10/PK 1 2° Cone: 272
Casson Viscosity @ 25°C, mPa•s (cP) Cone & Plate Rheometer: 30,000 to 60,000
Casson Base Viscosity , mPa•s (cP): Haake PK 100, M10/PK 1 2° Cone: 42,000
Tensile Strength, ISO 527-3 N/mm² (psi): 44 (6,380)
Tensile Modulus , ISO 527-3 N/mm² (psi): 1,460 (211,700)
Compressive Strength, ISO 604 N/mm² (psi): 62 (900)
Elongation , ISO 527-3,%: 5.8
Glass Transition Temperature, ASTM E 1640, °C: 133
Coefficient of Thermal Conductivity, ISO 8302, W/(m-K): 0.3
Primary Chemistry:
Epoxy
LOCTITE® EA 9514 is a high-impact epoxy adhesive with multi-substrate compatibility and high-strength bonding capabilities. Its thixotropic viscosity allows it to effectively fill gaps up to 3.0 mm with easy application, making it suitable for filter and magnet bonding applications. Upon curing when exposed to heat or induction curing, this adhesive forms a rigid bond with excellent physical properties, including high shear and peel strength, chemical and solvent resistance, and high impact tolerance.
Appearance: Grey, opaque paste
Specific Gravity @ 25°C: 1.42 to 1.48
Yield Point @ 25°C, Pa•s: Haake PK 100, M10/PK 1 2° Cone: 272
Casson Viscosity @ 25°C, mPa•s (cP) Cone & Plate Rheometer: 30,000 to 60,000
Casson Base Viscosity , mPa•s (cP): Haake PK 100, M10/PK 1 2° Cone: 42,000
Tensile Strength, ISO 527-3 N/mm² (psi): 44 (6,380)
Tensile Modulus , ISO 527-3 N/mm² (psi): 1,460 (211,700)
Compressive Strength, ISO 604 N/mm² (psi): 62 (900)
Elongation , ISO 527-3,%: 5.8
Glass Transition Temperature, ASTM E 1640, °C: 133
Coefficient of Thermal Conductivity, ISO 8302, W/(m-K): 0.3
Primary Chemistry:
Epoxy
Poor adherence of adhesive to difficult substrates and rough or poorly fitting surfaces
Poor aesthetic appearance of bonding line after cure
Filter and magnet bonding