Diakon® CLG902L
Diakon® CLG902L is a PMMA compound with a relatively high melt flow index. It has good tensile strength and is used in injection molding and extrusion.
Quantity
Documents
Specifications
Melt flow index, g/10 min: 7.3
Vicat softening point, °C (ISO 306A): 108
Vicat softening point, °C (ISO 306B): 102
Heat deflection temperature, °C (ISO 75A): 97
Heat deflection temperature, °C (ISO 75B): 100
Coefficient of expansion, cm/cm/°C x 10-5: 7.1
Light transmission, %: 92
Haze, %: 0.4
Refractive index: 1.49
Tensile strength, MPa: 80
Elongation flexural strength, %: 5.0
Flexural modulus strength, GPa (MPa): 3.0, 110
Izod impact strength, kJ/m2: 1.8
Charpy impact strength, kJ/m2 (ISO 179/1eA): 2.0
Charpy impact strength, kJ/m2 (ISO 179/1eU): 20
Relative density: 1.18
Rockwell hardness, M scale: 92
Ball indentation hardness, MPa: 180
Mold shrinkage, %: 0.4–0.7
Water absorption, %: 0.30
Flammability: HB
Glow wire test, °C: 650
Primary Chemistry:
PMMA
- Manufacturer: Mitsubishi Chemical Group
- Product Line: Diakon® and Elvakon® PMMA
- Product: Diakon® PMMA
- Industries: Plastics
- Authorized Countries: United States
Manufacturer
Product Line
Product
Industries
Authorized Countries
United States
Overview
Diakon® CLG902L is a polymethyl methacrylate (PMMA) compound that offers ease of processability through injection molding and extrusion. It features a relatively high melt flow index amongst Diakon® grades and is typically used in profile extrusion applications. Like other Diakon® PMMA grades, CLG902L is made from high-quality polymers that feature high light transmission and create high optical clarity. Parts made with Diakon® CLG902L have outstanding resistance to yellowing and discoloration. Examples of parts typically made with this grade include optical lenses, electronic component housings, and medical device parts.
Specifications
Melt flow index, g/10 min: 7.3
Vicat softening point, °C (ISO 306A): 108
Vicat softening point, °C (ISO 306B): 102
Heat deflection temperature, °C (ISO 75A): 97
Heat deflection temperature, °C (ISO 75B): 100
Coefficient of expansion, cm/cm/°C x 10-5: 7.1
Light transmission, %: 92
Haze, %: 0.4
Refractive index: 1.49
Tensile strength, MPa: 80
Elongation flexural strength, %: 5.0
Flexural modulus strength, GPa (MPa): 3.0, 110
Izod impact strength, kJ/m2: 1.8
Charpy impact strength, kJ/m2 (ISO 179/1eA): 2.0
Charpy impact strength, kJ/m2 (ISO 179/1eU): 20
Relative density: 1.18
Rockwell hardness, M scale: 92
Ball indentation hardness, MPa: 180
Mold shrinkage, %: 0.4–0.7
Water absorption, %: 0.30
Flammability: HB
Glow wire test, °C: 650
Primary Chemistry:
PMMA
Features & Benefits
- Extremely high optical clarity and light transmission
- High melt flow index
- Ideal for profile extruded parts
- Strong resistance to weathering and yellowing
Problems Solved
Poor light transmission through acrylic parts
Deterioration of clarity and color under exposure to harsh environments
Breaking of parts due to tensile or flexural stress
Applications
Injection molding
Extrusion
Related Chemistries
Plastics
Related End Markets
Related Functions
Plastics
Related Processes
Plastics
Have questions? Can't find the right product?
Ask our Experts
Have questions? Can't find the right product?
Ask our ExpertsWhen You're Ready
When You're Ready
View Support Articles
Talk to an Expert
Ask a Question
Are you in the correct region?
We’ve detected that you are located in a different region than the region selected on the website. Would you like to change your region?
Current Region: English - United States