Water Dispersible Sulfopolyesters - AQ™ Polymers & Eastek™

Eastman AQ™ sulfopolyester polymers, are solid, water-dispersible resins produced by polymerization using glycols and aromatic diacids. The same water-dispersible resins are available in a predispersed form under the Eastek™ trade name, allowing formulators the flexibility of working with a solid resin or water-based dispersion. 

When choosing a water-dispersible sulfopolyester resin, there are key physical properties to consider based on the application. The following sections provide an overview of the versatility of the AQ™ polymer and Eastek™ portfolios and the benefits they can provide. 

Viscosity
The viscosity of sulfopolyester dispersions depends on the percent solids of the dispersion. Unlike solution-based polymers like PVOH and PVP, dispersions of AQ™ polymers have a relatively low viscosity, resulting in less than 100 cP up to 30% solids. Above 30% solids, the viscosity will increase rapidly with concentration, similar to latexes. 

Minimum Film Forming Temperature and Drying Time
The minimum film-formation temperature of typical dispersions is usually equal to the Tg of the dispersed polymer. To reduce that temperature, a plasticizer or coalescent must be added. Sulfopolyesters are plasticized by water; therefore, the minimum film-formation temperature is about 20°C less than the Tg of the polymer. As such, sulfopolyester film formation will occur at relatively low temperatures without an additional plasticizer or coalescent. Compared to systems that may require plasticizers, such as polyurethane dispersions (PUDs) or acrylic emulsions, this feature offers formulators better cost savings. This lower film-formation temperature, coupled with the small nature of sulfopolyester polymer aggregates compared to PUDs and acrylic emulsions, lends to AQ™ polymers and Eastek™ dispersions having a very rapid drying time, which benefits coating, ink, and adhesive applications. 

Tack and Flexibility
AQ™ polymers and Eastek™ dispersions range in Tg from 3°C to 63°C, which allows formulators to select the optimal sulfopolyester grade depending on the end-use requirements of each coating, ink, or adhesive application. Sulfopolyesters with a Tg over 45°C form thin, rigid films with low tack. Inversely, sulfopolyesters with a Tg less than 35°C form flexible films with moderate tack. 

Water & Humidity Resistance
The water and humidity resistance of films formed by sulfopolyesters is inversely related to the charge density of the sulfopolyester polymer; low-charge-density polymers have higher resistance than high-charge-density polymers. Water resistance can also be increased or decreased by the addition of hydrophobic or hydrophilic plasticizers, respectively. Additionally, sulfopolyesters do not disperse in solutions with high ionic strength.  

Gloss
Sulfopolyester dispersions have very small particle aggregates. As a result, the films formed have a very smooth and glossy appearance. If a matte appearance is desired, conventional matting agents, such as clay or silica, work well with sulfopolyesters. 

Coatings & Inks
The broad Tg range of AQ™ polymers allows for formulating coatings and inks with customized flexibility and tack. Additionally, the rapid film formation of sulfopolyesters makes AQ™ polymers an ideal resin for formulators looking to increase the productivity of printing and coating operations. Eastek™ dispersions add convenience by being offered as a predispersed option. 

 

Hot Melt Adhesive
AQ™ 1950 was designed to be used as a thermoplastic resin in repulpable hot-melt adhesives. AQ™ 1950 has a low Tg, offering good tack, flexibility, and adherence to most common packaging films and paper. AQ™ 1950 has a very high charge density, making it readily dispersible in water. This makes hot-melt adhesives formulated with AQ™ 1950 completely repulpable and provides for easier recycling of packaging materials. 

Textile Sizing
The smooth and flexible nature of films formed from lower Tg sulfopolyesters make for excellent textile sizing.  Coatings made with Eastek™ 1000 and AQ™ 38S provide optimum flexibility and slip to protect yarns from the stress applied during weaving. Yarns sized with sulfopolyesters are stronger and will break or rupture less frequently, allowing for the increased productivity of weaving processes.