MOR-FREE™ 403A is a solventless, two component polyurethane adhesive that is used as a laminating adhesive for flexible packaging.
Fulfilled by ChemPoint
- Dow
- Dow Laminating Adhesives
- MOR-FREE™
-
Canada | United States
Product Overview
MOR-FREE™ 403A is a 100% solid, 2 part laminating adhesive that provides outstanding adhesion to metal and high slip films. It should be used with Coreactant C-411, C-117, or C-132-2. MOR-FREE™ 403A is typically used in flexible packaging applications that require good heat and chemical resistance like stand up pouches, condiment packaging, and confectionery packaging.
Product Specifications
Application Method: Smooth roll transfer Coreactant: C-411, C-117, C-132-2
Coating Weight: 0.8-1.2 lbs/ream
Chemistry: Polyurethane
Density: 9.8 lbs/gallon
Mix Ratio: 100:60 with C-411, 100:100 with C-117, 100:100 with C-132-2
Shelf Life: 360 days
Cure Time: 7 days @ 75 °F
Mixed Viscosity: 600 cPs @ 120 °F
Nip Temperature: 120-140 °F
Nominal Application Temperature: 122-140 °F Post Process Time: 14-24 hours time to slit
Pot Life: 25-30 minutes at 110 F
Substrates: Nylon, Aluminum, Polyester, Polyethylene, and other packaging substrates, unprinted or reverse printed. Viscosity 1,700 cPs at 77 °F
Coating Weight: 0.8-1.2 lbs/ream
Chemistry: Polyurethane
Density: 9.8 lbs/gallon
Mix Ratio: 100:60 with C-411, 100:100 with C-117, 100:100 with C-132-2
Shelf Life: 360 days
Cure Time: 7 days @ 75 °F
Mixed Viscosity: 600 cPs @ 120 °F
Nip Temperature: 120-140 °F
Nominal Application Temperature: 122-140 °F Post Process Time: 14-24 hours time to slit
Pot Life: 25-30 minutes at 110 F
Substrates: Nylon, Aluminum, Polyester, Polyethylene, and other packaging substrates, unprinted or reverse printed. Viscosity 1,700 cPs at 77 °F
Primary Chemistry: Isocyanate
Features & Benefits
Zero VOC
Excellent metal adhesion
High Chemical resistance
FDA 21 CFR175.105 Compliance
Low Nip Temperature
Heat Resistance
Excellent metal adhesion
High Chemical resistance
FDA 21 CFR175.105 Compliance
Low Nip Temperature
Heat Resistance
Problems Solved
Regulations that limit the use of adhesives with VOC content
Adhesion failure to metal and high slip films
Damage to adhesive bonds due to exposure to chemicals and heat
Adhesion failure to metal and high slip films
Damage to adhesive bonds due to exposure to chemicals and heat
Applications
Stand Up Pouches; Coffee Bags; Snack Food Packaging; Condiment Packaging; Confectionery Packaging